Advanced smart biomaterials and constructs for hard tissue engineering and regeneration
INTRODUCTION
In general,smart(or intelligent)biomaterials and constructs refer to those that:(1)possess instructive/inductive or triggering/stimulating effects on cells and tissues by Engineering the material's responsiveness to internal or external stimuli,such as pH,temperature,ionic strength and magnetism,to promote damaged tissue repair and regeneration;or(2)have intelligently tailored individual properties and controlled functions to actively participate in tissue regeneration in a valuable way.1-4This article reviews recent developments in smart biomaterials and constructs for hard tissue repair and regeneration.Hard tissues include bone and tooth enamel,dentin and cementum.Hard tissues are also termed calcified tissues,as they contain calcium phosphate minerals.The need for hard tissue repair and regeneration has substantially increased as the world population ages.5-6Bone fractures,defects and non-unions are a significant worldwide problem.7-8The annual healthcare costs plus lost wages for individuals in the United States with musculoskeletal diseases reached$849 billion in 2004 or 7.7%of the gross domestic product.8This cost is rapidly increasing as the population ages.Although autografts are the gold standard,the risks of donor site morbidity and limited availability restrict their applications.Allografts are impeded by potential infection and a high nonunion rate with host tissues.Therefore,smart biomaterials and smart tissue engineering constructs provide immense potential as an exciting alternative to autogenous bone grafts.5-6,9-10
Regarding the other hard tissue,tooth caries is the most prevalent disease in humans.Dental caries creates substantial public healthcare burdens and affects oral and general health and quality of life.11-12In the US,more than 200 million tooth cavity restorations are placed annually,costing$46 billion in 2005.12The need is rapidly increasing with increases in the life expectancy and tooth retention rates in seniors.13Caries is caused by acidogenic bacteria fermenting carbohydrates to produce acids,which leads to mineral loss.14Even after a tooth cavity is restored,the restoration often fails over time,mainly due to secondary(recurrent)caries.15Moreover,the replacement of failed restorations accounts for more than half of all restorations placed.16 Therefore,there is an immense need to develop a new generation of smart dental restorations to reduce and eliminate caries.This article covers both bone and teeth because many of the smart biomaterials and smart constructs are applicable to both types of hard tissues.
SMART SCAFFOLD CONSTRUCTS WITH STEM CELLS FOR BONE TISSUE ENGINEERING
Scaffolds,cells and growth factors are the three basic elements of bone tissue engineering.17Scaffolds are not only a substitute for the extracellular matrix(ECM)but can also serve as the delivery vehicle for cells and the carrier for growth factors.18Scaffolds affect seeded cells,including cell attachment,migration and proliferation,thus affecting the efficacy of regenerative medicine.19Smart scaffolds have been designed with the incorporation of bioactive molecules and nanoparticles and the use of tailored modifications of the physical and chemical properties of the scaffolds.20-21They can improve the interactions with cells by enhancing the osteogenic differentiation for bone repair and responding better to the surrounding host environment.3Scaffolds were composed of natural or synthetic materials or their combinations,and their advantages included that they could incorporate bone progenitor cells and growth factors to display osteoconductive and osteoinductive potentials and help replace and repair bone defects.The typical deficiencies of traditional scaffolds included material-related infections,mechanical failures and adverse immunogenic reactions with the host.Recent studies have developed novel smart scaffold constructs to improve the tissue regeneration efficacy.
Biomimetic and bionic smart scaffolds
An important class of smart materials is referred to as biomimetic smart materials.Their development is based on the biological inspiration of the structure,function and formation of biological materials.22Engineering multifunctionaland adaptive cellular microenvironments is imperative in developing native tissue-like biomaterials.The cell-biomaterial interface is a complex and dynamic microenvironment and is important in tissue regeneration.23Stem cells in contact with the scaffold can sense different properties,such as stiffness and nanostructure,and make the appropriate responses,thus enabling smart scaffolds to induce the desired cell responses.For example,previous studies have indicated that innate immune cells,particularly macrophages,could undergo phenotypical changes after being challenged by the tailored material cues,which could facilitate tissue regeneration.24
其中,yit表示城市群t年i城市的人均GDP,agg表示产业集聚水平,inn表示技术创新,Zit是控制变量,包括外商直接投资 (fdi)、政府干预度 (gov)、信息化水平 (xxh),μit是随机误差项。考虑到滞后一期的经济增长会对当期经济增长产生一定的影响,为体现经济增长的动态性,在模型中引入经济增长的一阶滞后项 (yit-1)。
Recently,smart artificial bone scaffolds were prepared to mimic the composition and structural characteristics of natural bone using the principles of biomimetics,nano-assembly technology and additive manufacturing techniques.25Specific molecular recognition signals,such as peptides,growth factors and genes,were immobilized on the scaffold.Biomimetic porous poly(lactideco-glycolide)(PLGA)microspheres coupled with peptides were used to construct biomimetic environments for tissue engineering.26Based on the analysis of the porous structures of trabecular bone,computer-aided porous scaffold design for tissue engineering could describe the surface morphology and pore size distribution of the bone microstructure.27Thus,the smart scaffold could closely mimic the true features of the skeleton and follow the complexity of the natural bone tissue structures in vivo,thereby holding substantial potential as guidance templates for cells to enhance bone regeneration.
Immune-sensitive smart scaffolds
However,scaffoldswith poorbiocompatibility can trigger aggressive foreign-body reactions in vivo.To avoid or lessen the potential immunological response between the host immune system and foreign scaffolds,it is important to develop smart immunomodulatory biomaterials that are capable of directing the host response towards tolerance of the foreign scaffolds or regulate immunological microenvironments to promote cell survival.The immune system is the first responder of the host and plays a critical role in responding to tissue trauma and the implantation of biomaterials.28The immune system consists of the innate and adaptive immune systems,which play key roles in combating disease and infection.Immune-sensitive smart scaffolds with an osteoimmunomodulatory capability could provide an osteoconductive microenvironment to enhance stem cell survival and regenerative functions.29
Surface modification of scaffolds could be beneficial for immune cell activation and infiltration.30ECM-like injectable gelatin microspheres were synthesized via the self-assembly of heparin-modified gelatin nanofibres.31-33Interleukin 4(IL4)was incorporated into the scaffold by binding the domains with heparin to protect it from denaturation and degradation,which helped prolong its sustained release to modulate the macrophage polarization.34The nanofibrous heparin-modified gelatin microspheres(NHG-MS)could spatiotemporally deliver the anti-inflammatory cytokine IL4 to polarize the proinflammatoryM1 macrophagesinto an anti-inflammatoryM2 phenotype,thus facilitating osteogenic differentiation and bone formation.34The release ofIL4 wasnotpH-or temperature-sensitive.However,the smart design was that the IL4 was incorporated into the nanofibrous gelatin microspheres through binding with heparin,which mimicked the binding of cytokines and growth factors with glycosaminoglycan in natural ECM.In addition,heparin had a specific binding domain with IL4.The smart binding of IL4 with heparin helped to stabilize and protectthe IL4 from degradation and controlled the sustainable release of the bioactive IL4 for up to 3 weeks.Furthermore,even under diabetic conditions,the IL4-loaded immunomodulatory microspheres significantly enhanced bone regeneration,as shown in a diabetes mellitus(DM)rat mandibular periodontal defect model in Fig.1.34The micro-computed tomography(µ-CT)analysis at 4 weeks after surgery demonstrated that the IL4-loaded NHG-MS restored the close to the normal level in the presence of diabetes.The defect area was entirely occupied by new bone in the nondiabetic control group(Fig.1a,b)and the IL4-loaded NHG-MS DM group(Fig.1g,h).In contrast,only half of the defect was filled with new bone in the DM(Fig.1c,d)and DM+NHG-MS groups(Fig.1e,f).The ratio of the bone volume to total volume(BV/TV)of the IL4-loaded NHG-MS DM group(0.44)was approximately twofold that of the DM+NHG-MS group(0.23)(Fig.1i).34
Figure 6b,c plot the Escherichia coli(E.coli)growth curves after treatment with pH 4.1 and pH 7.9 buffers.135At pH 4.1,a concentration of 2.5 µg·mL-1of Azo-QPS-C16 was suf fi cient to completely inhibit E.coli growth.In sharp contrast,at pH 7.9,40 µg·mL-1of Azo-QPS-C16 was required to completely inhibit E.coli growth.The bacteria were subsequently treated with Azo-QPS-C16 for 30 min using a 2-fold serial dilution.The effect of pH on the antibacterial potency of Azo-QPS-C16 in terms of the minimum bactericidal concentration(MBC)was then measured by inoculating cultures onto a Lysogeny broth agar plate.As shown in Fig.6d,the MBC increased with increasing pH.From pH 4.1 to 7.9,the MBC for E.coli was increased by 16-fold.A similar pH-sensitive antibacterial function was shown for the cariogenic Streptococcus mutans(S.mutans)(Fig.6d,third column).These results demonstrate that the smart pH-sensitive materials can selectively inhibit acid-producing bacteria,thereby providing protection against infection and erosion via targeted treatments againstacid-producing bacteria.These smartmaterialsare promising for applications not only in combating tooth caries but also in inhibiting the selected pathogens for orthopaedic implants and tissue engineering scaffolds.
![pagenumber_ebook=19,pagenumber_book=318](https://qkk.lw71.com/uploads/image/2018/4/e0068a2dca9632ca62be9120acd9a4d7.png)
Fig.1 Smart immunomodulatory microspheres(NHG-MS)accelerated bone regeneration in diabetes mellitus(DM).µ-CT at 4 weeks confirmed that bone regeneration was impaired by diabetes.However,IL4-loaded NHG-MS restored the bone regeneration to the healthy non-diabetic level.The defect was filled with new bone in the healthy non-diabetic control(a,b)and the IL4-loaded NHG-MS DM(g,h).In contrast,only half of the defect was filled with new bone in the DM(c,d)and DM+NHG-MS(e,f).i The ratio of bone volume to total volume(BV/TV)of the non-diabetic group was twice that of the DM group.IL4-loaded NHG-MS in DM rats increased the BV/TV ratio to 0.44,twofold that of the NHG-MS group(0.23).(**P<0.01).(Adapted from ref.34,with permission.)
In addition to the pH-triggered release of cavity- fi ghting ions,anothertype ofsmartbiomaterialspossesseson-demand antimicrobialcapabilityand can produce stimuli-responsive antibacterial activity on-site.They enable the treatment of infection locally with less antimicrobial agent,which can help reduce antimicrobial drug resistance.133-134Previous studies developed optically controlled antibacterial function to improve the efficacy of drugs via light irradiation.133-134In addition,the antibacterial function of a supramolecular complex was reversibly switched on band off through the assembly and disassembly of a cationic poly(phenylene vinylene)derivative.134Recently,pH-sensitive quaternary pyridinium salts(QPS)were developed,for which the antibacterial potency is boosted by low pH and can be controlled by varying the pH between 4 and 8.135This material can selectively suppress the growth of acidogenic bacteria within a multispecies biofilm.This molecule,(E)-1-hexadecyl-4-((4-(methacryloyloxy)phenyl)diazenyl)-pyridinium bromide(termed Azo-QPS-C16),can adjust its antibacterial potency within pH 4-8.Therefore,the biocidal activity of Azo-QPS-C16 can have localized triggering by acidic metabolic products of bacteria,which,in turn,leads to the killing of these bacteria.As shown in Fig.6a,135the antibacterial function is switched on via an acidic environment through the disassembly of the agglomerates,thus releasing Azo-QPS-C16.This increases the number of active antimicrobial sites,which is termed “antibacterial on”.In contrast,in a neutral or mildly basic environment,this process is reversed,which is termed “antibacterial off”.
Efforts were made to stimulate and harness the self-repair capacity for periodontal regeneration using biomaterials and biomolecules,such as growth factors.107Guided tissue regeneration(GTR)was the first generation of innate regeneration,which employed a membrane around the defect as a barrier to smartly prevent epithelial and fibroblast growth into the defect.This method helped maintain the space for bone and PDL regeneration,while recruiting host progenitor/stem cells to the wound.108 As infection was a main reason for periodontitis and clinical failure in regeneration,functional membranes were designed to respond to germs with antibacterial and anti-inflammation properties.97-98 A wide range ofantimicrobials,including amoxicillin and metronidazole,were added into the polymer membranes for periodontal repairs.97,110-112 For example, nanocomposite polycaprolactone-based membranes with amoxicillin were synthesized,which simultaneously provided antibacterial and osteoconductive properties.113Other alternative agents,such as chitosan,could also be incorporated into the membrane.114Moreover,chitosan could entrap biomolecules by crosslinking and ionic complexation and was thus used as a drug and growth factor carrier in periodontal regeneration.114-116Furthermore,collagen was combined with different crosslinking agents,biomaterials and cytokines to improve the mechanical properties and bioactivities,for example,by forming immune-responsive collagen membranes in GTR.98GTR yielded beneficial clinical outcomes in periodontal regeneration and was applied in clinical treatments.
BMP2-loaded shape-memory porous nanocomposite scaffold(SMP scaffold)that consists of chemically crosslinked poly(εcaprolactone)and hydroxyapatite(HA)nanoparticles was fabricated for the repair of bone defects.45The porous scaffold displayed shape-memory recovery from the compressed pores of 33μm in diameter to recover its original porous shape of 160μm in diameter,under both in vitro and in vivo conditions.In vivoµ-CT and histomorphometry results demonstrated that the BMP2-loaded SMP scaffold promoted bone regeneration in rabbit mandibular bone defects.45As shown in Fig.2,no mature bone trabecula was formed in the defect of the control group without a scaffold(Fig.2a,d).Newly formed bone within the defect was identified in the SMP scaffold group(Fig.2b).In contrast,nearly complete new bone and trabecula-like structures were formed in the BMP2-loaded scaffold group(Fig.2c,f).Quantification of neonatal bone in the defect at 8 weeks showed that the BMP2-loaded scaffold group generated the highest new bone percentage compared to the other groups(Fig.2h).45
Based on three-dimensional(3D)-printing technologies,fourdimensional(4D)-printed hierarchy scaffolds were created using a series of novel SMPs,demonstrating excellent biocompatibility and tunable shape-changing effects.464D printing refers to the 3D printing of active materials,such as SMPs,along with the fourth dimension (refers to time)to have time-dependent shape transformsafterprinting when exposed to environmental stimuli.46The smart polymeric scaffolds displayed fi nely tunable recovery and showed excellent attachment,proliferation and differentiation of MSCs.46Furthermore,4D shape-memory polyurethane scaffolds were also produced via 3D printing.47An intrinsic mechanical stimulus provided by controlling the timedependent morphing recovery of the scaffold was shown to significantly elongate the cells and the nuclei.Thus,the activity of cells seeded on SMP scaffolds could be effectively directed via multiple mechanical stimuli by optimally programming the cycle of shape recovery.47
Bone-forming peptide-1(BFP-1)-laden MSNs(pep@MSNs)were encapsulated into arginine-glycine-aspartic acid-treated alginate hydrogel(RA),which was referred to as pep@MSNs-RA.77MSNs contained many uniform and homogeneous pore channels;thus,they could be applied as an excellent drug carrier for BFP-1.The smart pep@MSNs showed a sustained peptide release pattern in the appropriate growth stage of hMSCs upon demand,with the initial osteo-inducing time likely on the fourth day.A smart sequencing stimulation on the osteo-differentiation of hMSCs was achieved,in which the survivability,spreading,expansion and aggregation of hMSCs was promoted by an adhesion ligand(RGD)-modified alginate matrix at an early stage.The osteogenic factor(BFP-1)release from pep@MSNs subsequently induced the osteo-differentiation.77The different functional time of BFP-1 could be regulated by changing the pep@MSN concentration in the gel.Furthermore,an in vivo test examined bone regeneration via pep@MSNs-RA encapsulated with hMSCs,with hMSC-loaded untreated hydrogelasthecontrol(UA),forsubcutaneous implantation in nude mice.77In Fig.3a,various gels(including UA,RA,pep-RA and pep@MSNs-RA)encapsulated with hMSCs were subcutaneously implanted into nude mice.In Fig.3b,different hMSC-loaded gels following removal from mice at 2 and 4 weeks after surgery are shown.Theµ-CT analysis results in Fig.3c shows that there was little mineralization in the groups at 2 weeks.At 4 weeks,mineralized bone was identified in pep@MSNs-RA,which was approximately 300-fold higher than the control group by quantitative bone volume analysis.77Alizarin Red-S staining in Fig.3d supported theµ-CT analysis.77These results indicate that the time-responsive dual-peptide delivery pep@MSNs-RA provided a niche-like native ECM,which enhanced stem cell growth to form mature bone.
![pagenumber_ebook=20,pagenumber_book=319](https://qkk.lw71.com/uploads/image/2018/4/5f891362f24f413c57545efcab6fc1b1.png)
Fig.2 BMP2-loaded shape-memory scaffold promoted bone formation:a-c HE staining;d-g Masson staining;and h quantification.The defect in the control(no scaffold)was full of granulation tissues(a).There was more neonatal bone in defects in the scaffold group(b,e).BMP2-loaded scaffold group(c,f)had the greatest amounts of new bone and mature bone.g High magnification Masson staining showed many multinuclear cells.h BMP2-loaded scaffold group had the greatest new bone percentage based on quantitative analysis(*P<0.05).(Adapted from ref.45,with permission.)
In addition,another important class of smart materials consists of electromechanical-stimulus scaffolds.The discovery of electric fields in biological tissues has led to the development of technologies that utilize electrical stimulation for therapies.48 The piezoelectric effect is the ability of certain materials to generate an electric charge in response to an applied mechanical stress.49Piezoelectricmaterials include certain crystals and ceramics,some living tissues(such as natural bone,tendon,ligaments,cartilage,skin,dentin and collagen)and certain biological macromolecules(such as proteins,nucleic acids and mucopolysaccharides).49Biological electric fields in host tissues play significant roles in functions that include neuromuscular activity,glandular secretion,cell membrane function,and tissue growth and repair.50Efforts were made to develop smart electrically active biomaterialsand scaffolds,demonstrating potential for bone engineering by providing electrical stimulation to cells to promote tissue formation.51
Piezoelectric materials enhanced tissue formation by providing an electrically active microenvironment without the need for external power sources for electrical stimulation.52-53Piezoelectric poly(vinylidene fluoride-tri fluoroethylene)(PVDF-TrFE)was fabricated into flexible,3D fibrous scaffolds.54The scaffolds stimulated MSC differentiation and tissue formation when undergoing dynamic loading,which mimicked the physiological loading conditions in structural tissues in vivo.54The piezoelectric scaffolds with dynamic compression at 1Hz frequency with 10%deformation induced greater MSC chondrogenic differentiation than mechanical loading alone.Histological staining clearly showed chondrocyte morphology and intense proteoglycan staining,as well as collagen type II immunostaining for electrospun PVDF-TrFE after 28 days,which was not detected in the control.Similarly,MSC osteogenic differentiation was promoted on piezoelectric scaffolds,with Alkaline phosphatase activity(ALP)and mineralization fivefold those for the control.54These results are consistent with another study showing that an electrospun PVDF-TrFE fibre scaffold containing zincoxide nanoparticlespromoted the adhesion and proliferation of human MSCs(hMSCs)and enhanced the blood vessel formation in a rat model.55
Furthermore,piezoelectric HA/barium titanate(BaTiO3)composite was fabricated and exposed to a dynamic loading device that simulated the force of human motion.56This provided periodic loading to the piezoelectric material while co-culturing with osteoblast cells.56When cyclic loading was applied on HA/BaTiO3,the electrical stimulation promoted osteoblast proliferation and growth,which was similar to the piezoelectric effects on human bone growth,modelling and reconstruction in vivo.56Therefore,electromechanical-stimulus smart scaffolds are promising for culturing with stem cells to enhance bone repairand regeneration.
SMART DRUG DELIVERY FOR BONE TISSUE ENGINEERING
![pagenumber_ebook=21,pagenumber_book=320](https://qkk.lw71.com/uploads/image/2018/4/740d185dfcd277ef664beb95e3f83dbe.png)
Fig.3 Smart dual-peptide alginate nanoscale drug delivery(pep@MSNs-RA)promoted bone mineralization.a Hydrogels(UA,RA,pep-RA and pep@MSNs-RA)encapsulated with hMSCs were subcutaneously implanted in nude mice.b hMSC-loaded gels following removal from mice at 2 and 4 weeks after surgery.cµ-CT reconstruction at 2 and 4 weeks.Little mineralization occurred in the groups at 2 weeks.At 4 weeks,RA,pep-RA and pep@MSNs-RA exhibited mineralization;substantially more mineralized bone tissues were identified in the pep@MSNs-RA group.d ARS staining.Minerals occurred in the hMSC-loaded groups(RA,pep-RA and pep@MSNs-RA),while no mineral occurred in UA(**P<0.01).(Adapted from ref.77,with permission.)
In addition to the ability of smart scaffolds to interact with cells and induce the desired cell functions for tissue regeneration,scaffolds can also be used to deliver drugs.Bioactive factors,including small molecules,cytokines,peptides,proteins and genes,can be loaded in drug delivery systems(DDS).57These smart systems can have controlled drug release and exert synergistic effects from multiple loaded drugs to enhance osteoblast proliferation and differentiation to promote bone regeneration.58-59Severaltypesofstimuli-responsive smart materials have been developed for drug delivery.60-61In addition,strategies are being investigated to spatially and temporarily control the delivery patterns of bioactive factors to optimize bone engineering efficacy.With the help of the controlled and targeted DDSs,the drugs incorporated into the smart systems could be delivered to the exact location with the correct dosage.This approach providesthe tailored spatio-temporaldeliveryof therapeutic agents,thereby minimizing the side effects and maximizing the therapeuticefficacy.However,these DDSs exhibited several shortcomings,including potential cytotoxicity,limited biodegradability and potential adverse immune responses,which warrant further investigation to overcome.
Stimuli-responsive tunable DDSs
阿里见阿东哭,便止住了自己的哭泣。他从未见过阿东哭,有些惊讶,也有些难过。他走过去,用手擦着阿东脸上的泪说:“你莫哭。我又要哭了。”说得阿东几乎想要号啕。
One novel strategy employs stimuli-responsive tunable DDSs.These materials can change their properties induced by a small stimulus;thus,they can deliver the required amount of drug ondemand by responding to the endogenous and/or exogenous stimulus.62Examples of exogenous stimuli include an electric field,magnetic field,ultrasound,electromagnetic radiation and temperature,which may be used to turn on or off the drug release from the carriers.63-64Examples of endogenous stimuli include pH,temperature,ionic environment,proteins and carbohydrates.63-64
Stimuli-responsive smart materials were developed that could enable real-time non-invasive or minimally invasive drug delivery and monitoring.65Polymers with controlled,tunable and reversible responses to environmental stimuli were shown to be excellent candidates for drug delivery.66In addition,smart hydrogel DDSs with predictable and tunable drug release and degradation rates were developed.67-68A novel pH-responsive bacterial cellulose-g-poly(acrylic acidco-acrylamide)hydrogel with a highly porous morphology was developed as an oral controlledrelease drug delivery carrier.67The intelligent hydrogel was demonstrated to exhibit remarkable pH-responsive changes in swelling behaviour,with decreased swelling in acidic media and maximum swelling at pH 7.Thus,these hydrogels could be suitable candidates for controlled drug delivery responding to pH changes in the host physiological environments.Another poly(ethylene glycol)hydrogel was loaded with drugs by β-eliminative linkers and demonstrated tunable capability in drug release and the hydrogel erosion rate,showing good potential for applications in regenerative medicine and orthopaedic implants.68In addition,farnesol-loaded nanoparticles,composed of 2-(dimethylamino)ethyl methacrylate(DMAEMA),butyl methacrylate(BMA)and 2-propylacrylic acid(PAA)(p(DMAEMA)-b-p(DMAEMA-co-BMA-co-PAA))were synthesized with a pH-responsive drug release capability due to microenvironmental triggers.69They were tuned to expedite the drug release when the local cariogenic biofilm microenvironmental pH became acidic at pH 4.5.This suggested that the tunable nanoparticle-mediated drug delivery approach could be used to deliver drugs to treat and respond to biofilmrelated infections.Furthermore,a dual-responsive DDS was developed by coating electro-sensitive and thermally responsive functional macromolecules to mesoporous silica nanospheres.70 This system could act as a rate modulator to regulate the diffusion kinetics of the drugs loaded in the channels of the inorganic nanocarriers.70The released quantities could be continuously tuned by changing the frequency of the applied external electric field under different temperatures.These smart and tunable DDSs with a flexible modulation capability of the release quantity have great potential in biomedical engineering and tissue regeneration applications.
Smart multifunctional nanoparticle-based DDSs
Another strategy consists of multifunctional nanoparticle-based drug delivery.With the advancements in nanotechnology,various nanoparticles with dimensions of 10-200nm are recognized as promising drug transport vehicles due to their favourable biological properties,small size and high surface area,surface chemistry and the ease with which they are taken up by cells.71 Typically,drugs,growth factorsand geneticmaterialsare entrapped or encapsulated in,or attached to,the nanoparticles for delivery.72-73One type of nanoparticle for drug delivery included mesoporous silica nanoparticles(MSNs).MSNs had variable pore structures and large active surface areas,which enabled the attachment of different functional groups to achieve precisely controlled drug release and targeted delivery.74These nanoparticles were imparted with smart features to better react to the biological environment and meet the on-demand therapeutic and diagnostic purposes of diseased and damaged tissues.Multifunctional nanomaterials were proposed to enable the simultaneous target imaging and on-demand delivery of therapeutic agents to the specific tissue site.22Stimuli-responsive controlled-releaseMSNsweredesigned thatresponded to internal stimuli,including enzymes,pH and temperature,as well as external stimuli,including light,ultrasound and magnetic fields.75-76
总而言之,青年工作的开展是一项系统性工程。中国特色社会主义新时代的巨大成就为青年的成长成才创造了丰富的精神财富和坚实的物质基础,为青年发展奠定了稳固“基石”,而科学而系统的青年发展的政策框架,则进一步为青年发挥能量,建功立业提供了很好的机会和保障,让每个青年人都能够找到合适的方式,来奋斗青春,大展宏图。
Electromechanical-stimulus smart scaffolds
Biomimetic DDSs
Furthermore,another key strategy developed biomimetic DDSs.Faced with the complexity of the native tissue microenvironment and adverse side effects,biomimicry is receiving increasing attention.78Compared with traditional DDSs,biomimetic materials could imitate the intricate ECM composition and architecture,thus providing a molecular platform to enhance the control over the delivery of therapeutic molecules,bioactive cues and instructive signals.79-80Biomimetic biomaterials with biological and physicomechanical features inspired by the natural ECM were shown to be able to regulate tissue regeneration.81Biomimetic hydrogels,biomimetic micelles,biomimetic liposomes,biomimetic dendrimers,biomimetic polymeric carriers and biomimetic nanostructures were developed.82-83They mimicked the natural ECM to provide a desirable cellular environment to support cell growth and biodegradation.84Furthermore,biomimetic peptide-based,self-assembly hydrogels(RADA16)were used as an intraosseous delivery vehicle for BMP2 into defects within the femoral head model,thus promoting osteoblastic differentiation of BMSCs and bone remodelling.85Thiswasachieved byactivating the phosphorylation of SMAD 1/5/8,a well-established upstream indicator of the BMP2 signalling cascade and a precursor to osteoblastic gene transcription.85In addition,considering the benefits of hollow-channel materials to promote vascularization and the advantages of the unique structure in lotus roots,lotus root-like biomimetic materials with parallel multi-channels were fabricated via a modified 3D printing strategy.86Compared with traditional 3D-printed scaffolds,these biomimetic lotus root-like structures could successfully induce blood vessels and new bone tissues to grow into the inner locations of the biomimetic materials and effectively promote bone defect healing.Therefore,these smart scaffolds possessed better angiogenic and osteogenic stimulatory capabilities,with substantial potential for cell delivery and bone regeneration applications.86
One important smart stimuli-responsive approach in dentistry employs materials that can respond to pH to protect the tooth structures.Dental caries is prevalent worldwide,is one of the most common bacterial infections in humans and represents a heavy financialburden.122-123The basic mechanism of caries is demineralization due to attack by acid produced by bacteria.123-125Oral acidogenic bacteria ferment carbohydrates and produce organic acids,including lactic,formic,acetic and propionic acids.123Following a sucrose rinse,the local plaque pH can decrease to 4.5 or 4.126Regarding the protection of tooth structures,there is a critical pH below which demineralization dominates,causing mineral loss.127For most individuals,this critical pH is approximately 5.5.126The Stephan Curve shows that the plaque pH,following a glucose rinse,remains in the cariogenic area of close to pH 4 for approximately 30 min and then increases back to a safe pH of>5.5 after the bacteria have completed their metabolization of the glucose and the saliva has buffered the acid.126Therefore,it would be highly desirable to develop a smart resin for tooth cavity restorations that responds to pH by releasing high levels of calcium and phosphate ions and neutralizing the acids at a low pH when these ions are most needed for caries inhibition.Moreover,when the pH is close to neutral,the smart resin would have little release to preserve the ion reservoir.
SMART BIOMATERIALS AND CONSTRUCTS TO PROMOTE DENTAL AND PERIODONTAL REGENERATION
Anotherimportantapplication forsmartbiomaterialsand constructs is periodontal regeneration.Periodontitis is a prevalent chronic inflammatory disease and the leading cause of tooth loss.87-88Periodontitis is initiated by microbes;it leads to periodontal supporting tissue destruction and eventually tooth loss,which significantly affects the quality of life and is a worldwide health burden.89However,the regeneration of periodontal tissues remains a major challenge due to the complexity of the hierarchical architecture of the periodontal ligament(PDL)interspersing between thetooth rootcementum and the anchoring bone,oral hygiene,oral fluids,bacterial infection,etc.In addition,the damaged periodontal tissues have a poor innate ability to regenerate.Therefore,there is an urgent need to develop smart materials that can respond to the infection,stimulate the innate regenerative capability and mimic the original architecture and function of the periodontium.90
自2012年全面启动新型职业农民培育工作以来,农业农村部制定了一系列支持新型职业农民培育和发展的文件,明确了新型职业农民的培育原则,细分了培育类型和标准。尤其在“十三五”中,把习总书记提出的“坚持把科教兴农、人才强农、新型职业农民固农”作为农业农村发展的重大战略,也为新型职业农民培育工作指出了方向。
Previous studies have focused on alveolar bone remodelling(including bone formation and resorption)in the bone microenvironment to promote the osteogenic differentiation of stem cells or decrease the differentiation and activity of osteoclasts,with the aim of enhancing alveolar bone regeneration.91-96Other studies attempted to activate the host innate ability,recruit host stem cells to the defect and promote their differentiation,and create an advantageous microenvironment for reducing inflammation and accelerating the bone-healing process.97-99More recent studies focused on the unique structure of the periodontium,with efforts to imitate the structure by designing multiphasic scaffolds to regenerate the PDL and the entire periodontium.100-106
Another class of smart scaffolds have a shape-memory capability.Shape-memory polymers(SMPs)can return from a deformed shape to their original shape by an external stimulus,such as temperature change,37an electric or magnetic field,38-39and light.40They have received substantial attention as a result of their applications in tissue engineering.41The advantages of the shapememory behaviour are that the scaffolds can be predesigned,deformed to be conveniently implanted into bone defects via minimally invasive surgery and then expanded to adapt to an irregular bone defect.42The initial implant has a small size and can be deployed in the body using minimally invasive means with the least damage to host tissues.After deployment,the implant regains a larger shape to fill the bone defect,even precisely matching irregular bone defect boundaries.43-44
There were reports of excessive immune responses to periodontal bacteria,117and macrophages played a basic role in the onset and progression of periodontitis.117-118Therefore,smart materials were designed to target the macrophages in a harnessing manner to control the inflammation and enhance the innate regeneration.A previous study focused on the immunomodulatory effect of stem cells from human exfoliated deciduousteeth (SHEDs)on the macrophage phenotypic switch.119It was found that SHEDs could promote the classically activated M1(promote inflammation)to alternative M2(inhibit inflammation),thereby decreasing the local inflammation and enhancing periodontal regeneration.119Another study investigated microspheres self-assembled with heparin-modified gelatin nanofibres and showed that the microspheres acted as an osteoimmunomodulatory scaffold,producing a pro-regenerative microenvironment for periodontal regeneration under DM.99
Furthermore,the functionally oriented PDL inserting into cementum and alveolar bone,as well as the interplay of these three types of tissues,pose a major challenge for tissue engineering.One approach to address this challenge was the development of multiphasic and multi-layered scaffolds that mimic the structure and property of the different tissues.102Bilayered,biphasic,hybrid,triphasic scaffolds were developed to utilize two or three different architectures,materials and composites for periodontal regeneration.100-101,103-104,106-107,120Other technologies,including cell sheets,3D printing,electrospinning and electrospray,were used in developing multiphasic scaffolds for periodontal regeneration.100-101,103-104,106-107,120 In particular,bilayered poly(lactic-co-glycolic acid)(PLGA)/calcium phosphate constructs were applied in periodontal defects in beagle dogs.107A biphasic scaffold composed of a bone compartment(a fused deposition modelling scaffold)and a PDL compartment(an electrospunmembranecombinedwithPDLSCsheet)were designed for simultaneous PDL and alveolar bone regeneration.107 In addition,a tri-layered nanocomposite hydrogel scaffold was developed.To fully mimic the structure of the periodontium,the scaffold consisted of the alveolar bone phase of chitin-PLGA/nanobioactive glass ceramic(nBGC)/platelet-rich plasma derived growth factors,as well as the PDL phase of chitin-PLGA/ fibroblast growth factor and the cementum phase of chitin-PLGA/nBGC/cementum protein 1.121The multiphasic scaffolds were promising in inducing cells for cementogenic differentiation onto tooth root surfaces,encouraging PDL alignment to the cementum and bone,and providing osteogenesis signals for bone formation.121However,the natural structure and physical and chemical properties of the periodontium remained difficult to mimic.The adaptation of the scaffold on the interface between the different types of tissues remained poor,and the material's resorption rate and the tissue regeneration rate remained difficult to match.Therefore,further studies are required to improve the multiphasic/multi-layered scaffolds,optimize cell and growth factor delivery and their tailored interactions,and undertake animal studies on periodontal regeneration to translate the smart tissue engineering constructs from the laboratory to the clinic.
SMART DENTAL RESINS THAT RESPOND TO pH TO PROTECT TOOTH STRUCTURES
桩西潜山带位于沾化凹陷东部,在沾化、桩东、埕北3凹陷的交汇处,勘探面积220km2,构造上处于埕岛、长堤、埕东三大断裂体系的应力交汇处,断裂系统极为发育,地质构造格局复杂多样。
![pagenumber_ebook=24,pagenumber_book=323](https://qkk.lw71.com/uploads/image/2018/4/b931f4f67788b8bffd88e95cce22cae7.png)
Fig.4 Smart dental composites for caries inhibition.a Composites with calcium(Ca)ion release.The phosphate(P)ion release had a similar trend.Ion release substantially increased at a cariogenic pH 4 when these ions were most needed to combat caries.There was little release at a neutral pH to preserve the ion reservoir.b Remineralization.Dentin lesions withoutcomposite had substantial mineral loss.Dentin lesions restored with commercial composite had little remineralization.The smartcomposites caused successful remineralization.(Adapted from ref.128,with permission.)
Dentalresin compositeswere developed thatexhibited substantial calcium ion release at a cariogenic pH 4 and limited ion release at pH 7(Fig.4a).128Phosphate ion release showed a similar trend.128The two composites in Fig.4 consisted of nanoparticles of amorphous calcium phosphate(NACP)with a mean particle size ofapproximately116 nm,which were synthesized using a spray-drying technique,129in addition to tetracalcium phosphate particles with a median of 0.8μm.These composites were tested in dentin caries restorations in vitro,and the constructs were subjected to a cyclic demineralization and remineralization regimen for 4-8 weeks.128Transverse microradiography was performed to measure the mineral content in dentin,and the percentage of mineral change was used to determine the remineralization in Fig.4b(mean±SD;n=15).Due to the cyclic regimen of 23 h in pH 4 and 1h in pH 7 daily,the dentin lesion without a composite had mineral loss at 4 weeks(-55.7±20.3)%and 8 weeks(-100.66±35.8)%.A commercial composite(TPH)caused no remineralization as expected.In contrast,the smart composites achieved approximately 50%remineralization for the dentin lesions in 8 weeks.128In addition to dentin,a separate study demonstrated enamel remineralization by smart composite that was fourfold the remineralization achieved by a commercial fluoride control.130
![pagenumber_ebook=24,pagenumber_book=323](https://qkk.lw71.com/uploads/image/2018/4/0ddcbc9e173b876fce56d4fa7035d908.png)
Fig.5 Effect of smart resins on neutralizing biofilm acids and increasing the pH to avoid tooth decay.The adhesive resin contained MPC,DMAHDM and NACP from 0 to 40%.A dental plaque microcosm biofilm model was used with human saliva as inoculum.The pH of the biofilm medium with resin that contained 30 and 40%NACP was at pH 6 or greater.The pH of the biofilm medium with commercial adhesive was cariogenic at approximately pH 4,which could demineralize the tooth structures.(Adapted from ref.132,with permission.)
Moreover,a human in situ study was performed in which 25 volunteers wore palatal devices that contained enamel slabs with cavities restored using a smart NACP composite or a control composite,where the restorations were covered with biofilms in vivo fed with sucrose to produce acids.131The enamel mineral loss at the restoration margins around the smart composite was only 1/3 of the mineral loss around the control composite.131The mechanism of caries inhibition for the smart resins was demonstrated in a recent study,in which the pH of the biofilm medium was monitored.131In this study,a smart adhesive resin contained NACP, antibacterial dimethylaminohexadecyl methacrylate(DMAHDM)and protein-repellent 2-methacryloyloxyethyl phosphorylcholine(MPC).As shown in Fig.5,132the oral biofilm pH decreased with increasing time due to acid production by the biofilms and reached a cariogenic pH 4.0 for the commercial control adhesive,pH 4.1 for the experimental control(no DMAHDM,no MPC and no NACP)and pH 5.6 for the adhesive resin with MPC+DMAHDM+0%NACP.For the smart resins that contained NACP,the biofilm pH increased with an increasing NACP mass fraction and reached pH 6 with 30%NACP and pH 6.5 with 40%NACP at 72h.132These pH values are well within the safe zone of>5.5 to suppress caries formation.Further studies are required to investigate smart materials that respond to pH for dental applications,as well as for bone repair and regeneration,for example,to release calcium and phosphate ions triggered by overactive osteoclasts to potentially neutralize acids and suppress osteoporosis.
步骤2,延迟缓冲器的下界确定后,我们重新进行采样.对于每一次采样,最小化需要的延迟缓冲器的数量,并且使它们的调整值向中心值逼近.这一步,因为下限已经确定,取调整值的均值就可以反映出调整值的趋势.因此,压缩调整值以接近其均值的方法可以缩小延迟缓冲器的面积损耗.最后,延迟缓冲器的面积由最小和最大调整值决定.
![pagenumber_ebook=25,pagenumber_book=324](https://qkk.lw71.com/uploads/image/2018/4/62eb90c6ce39b9181a5170eea4fec0c1.png)
Fig.6 Smart pH-sensitive material for selective inhibition of acid-producing bacteria.a pH-sensitive,reversible spectroscopic properties and assembly behaviour of Azo-QPS-C16.The schematic shows the assembly and disassembly between Azo-QPS-C16 and its nano-sized aggregates,mediated by pH switch or addition of base/acid,for reversible control of the antibacterial activity.Acid-enhanced the antibacterial behaviours of Azo-QPS-C16,with E.coli growth curves after treatment with different concentrations of Azo-QPS-C16 at b pH 4.1 and c pH 7.9.d MBC values of Azo-QPS-C16 against E.coli and S.mutans at different pH values.(Adapted from ref.135,with permission.)
SMART PH-SENSITIVE MATERIALS TO SELECTIVELY INHIBIT ACID-PRODUCING BACTERIA
Shape-memory smart scaffolds
针对岩心冲蚀扰动的问题,可采取超前压入提前保护底部岩层以及避免冲洗液直接冲刷底部岩层的方式辅助内筒单动来解决。
![pagenumber_ebook=26,pagenumber_book=325](https://qkk.lw71.com/uploads/image/2018/4/898086117a3475a7285d657917580c1c.png)
Fig.7 Smart composite to shift species in biofilms towards a healthy composition.Three-species biofilms(S.mutans,S.sanguinis and S.gordonii)were grown on composites for 48 and 72h.The commercial composite was Heliomolar(Ivoclar).The DMAHDM wt%was varied in the experimental composite from 0 to 3%.The cariogenic S.mutans had overwhelming proportions for the commercial control and 0%DMAHDM group.With increasing DMAHDM wt%,the proportion of S.mutans sharply decreased,whereas S.sanguinis or S.gordonii achieved a predominant proportion.Values with dissimilar letters are significantly different(P<0.05).(Adapted from ref.146,with permission.)
In addition,an amino-functionalized bioactive glass(MBG)scaffold was developed to investigate its effects on bone marrow mesenchymalstem cells(BMSCs)and macrophages.35The osteogenic ability of the MBG scaffold was enhanced via amino functionalization and could coordinate BMSCs and macrophage differentiation.The osteoimmunomodulatory capability of the scaffold was endowed by the amino functionalization.35Furthermore, β-tricalcium phosphate(β-TCP),with reported favourable osteoimmunomodulatoryproperties,wasusedtocoatMg scaffolds to modulate the detrimental osteoimmunomodulatory properties of Mg scaffolds.36β-TCP-coated Mg scaffolds induced macrophages to switch to the extreme M2 phenotype,which caused the release of anti-inflammatory cytokines and osteoinductive molecules by the macrophages.This yielded an upregulation of bone morphogenetic protein(BMP)expression by 25-fold and enhanced the osteogenesis of BMSCs.36Therefore,osteoimmunomodulatory smart biomaterials have displayed favourable osteoinductive properties.Additional efforts should be devoted to endow the bone biomaterials with favourable osteoimmunomodulatory properties to trigger the desired immune response and promote bone regeneration.
SMART RESINS TO MODULATE BIOFILM SPECIES TOWARDS A HEALTHY COMPOSITION
Another class of smart materials aims to modulate the oral biofilm composition by suppressing cariogenic and pathological species and promoting non-cariogenic and healthy species.Quaternary ammonium methacrylates(QAMs)are cationic compounds with a broad spectrum of antimicrobial effects.136-139The antimicrobial mechanism of QAMs occurs via the disruption of bacterial membranes.136-139Compared to release-based biomaterials,QAMs can be co-polymerized with the resin matrix to anchor itself into the polymer network with prolonged functions.The first QAM used in dental resin was 12-methacryloyloxy dodecyl pyridinium bromide(MDPB),which exerted potent antibacterial effects against biofilm growth on resins.137-139Several other QAMs were subsequently developed,including quaternary ammonium polyethylenimine,140methacryloxylethyl cetyl dimethyl ammonium chloride(DMAE-CB),141dimethylaminododecyl methacrylate(DMADDM),142and DMAHDM.143-144
The dental plaque contains multispecies microbial communities.Variation in the oral environment can trigger a species change in the micro fl ora.Frequent sugar intake can promote the acidogenic and aciduric species at the expense of the healthy and less aciduric residents,thereby shifting the dental plaque towards a cariogenic composition.145Therefore,it would be highly desirable to develop smart resins to modulate the biofilms from a cariogenic state and shift it towards a non-cariogenic microbial community.This important direction of research has only recently been initiated and is in its early stage.A literature search indicated only one report on the use of QAM to modulate oral biofilms.145This study demonstrated that a resin containing DMADDM was able to suppress the cariogenic S.mutans and promote the growth of non-cariogenic species.145In addition to this published study,another study(in press)on a DMAHDM composite showed that it suppressed cariogenic species and promoted non-cariogenic species in oral biofilms.146A biofilm model that consisted of S.mutans,Streptococcus sanguinis(S.sanguinis)and Streptococcus gordonii(S.gordonii)wastested by growing biofilmson composites for 48 and 72 h.As shown in Fig.7,at 48 h,the commercial control and the experimental composite with 0%DMAHDM had S.mutans proportions of 73%and 69%,respectively.The S.mutans proportion decreased with an increasing DMAHDM mass fraction,accounting for 15%in the 2.25%DMHADM group and 10%in the 3%DMHADM group.At 72h,S.mutans in the commercial control and 0%DMAHDM group reached overwhelming proportions of 92%and 91%,respectively.In contrast,the S.mutans proportion decreased to 20%in the biofilm on the composite with 3%DMHADM.Moreover,the proportionsofnon-cariogenicS.sanguinisand S.gordonii increased with an increasing DMAHDM content.Therefore,the DMAHDM composite has the potential to modulate the biofilm composition shift from a cariogenic state to a non-cariogenic state.Further studies are required to develop smart biomaterials to suppress pathogenic species and promote healthy species in biofilms not only for dentistry but also bone regeneration and tissue engineering applications.Forexample,itwould be beneficial to develop smart constructs for periodontal regeneration that can suppress periodontal pathogens and promote healthy species to combat the progression of periodontal diseases and infections,which warrants further studies.
Lock the fault joint when it is adjusted to the desired locked angle,unlock joints J3-J7,and then regard links L1and L2 as a new link bound together.
SMART TAILORING OF ALKYL CHAIN LENGTH IN QAM TO AVOID DRUG RESISTANCE
While it is beneficial for dental resins to be able to suppress bacteria and modulate biofilms,it is important that they do not induce drug resistance.Frequent use of antibiotics may lead to a selection of resistant strains or the emergence of acquired resistance to these sensitive strains.147Bacterial drug resistance is a significant and increasing concern.147Previous studies have indicated that Staphylococcus aureus(a common cause of skin infections,respiratory infections and food poisoning),Serratia marcescens(involved in hospital-acquired infections,such as urinary tract infections and wound infections)and E.coli(occasionally responsible forproductrecallsdue to food contamination)could acquire resistance againstquaternary ammonium compounds.148-149
笔者认为,上述问题的思考和解决,对于挖掘几何课程的育人价值具有根本的重要性.例如,在97版教材中,直接说“根据两个平面平行及直线和平面平行的定义,容易得出下面的结论:α∥β,a⊂α,a∥β”,给出了结论确实是“容易”理解,但如果要让学生自己“这样去思考”、“如此去发现”,那么就绝非“容易”,因为这里涉及对“什么叫位置关系的性质”的理解,是在数学基本思想指导下的发现活动,而这正是这个内容所蕴含的育人价值之所在.
Research on the possibility oforalbacteria developing resistance to QAMs is only in the early stage.A literature search indicated that to date,there are only three publications on this important topic.150-152One study showed that after serial exposures to cationic biocides,S.mutans and Enterococcus faecalis(E.faecalis,which is closely associated with apical periodontitis)did not exhibit resistance to MDPB after repeated exposures,while E.faecalis developed drug resistance to chlorhexidine(CHX).150 Another study showed that DMAHDM did not induce drug resistance,while DMADDM and CHX induced drug resistance for S.gordonii by testing repeated exposures for 10 passages.151 Another study investigated the drug resistance against DMAHDM by further increasing the repeated exposures to 20 passages,with each passage using the exposed and survived bacteria as inoculum for the subsequent passage.152As shown in Fig.8a,for DMADDM,the minimal inhibitory concentration(MIC)of planktonic S.gordonii increased from 12.5 to 25 µg·mL-1at passage 5 and remained at 25 µg·mL-1until passage 20.For CHX,the MIC increased from 3.9 to 7.8 µg·mL-1at passage 7 and then remained constant until passage 20.In contrast,the MIC remained constant at 3.125 µg·mL-1for DMAHDM.Therefore,DMADDM and CHX induced bacterial resistance in S.gordonii;however,DMAHDM did not induce drug resistance.In Fig.8b,for each passage,the addition of DMAHDM into the resin substantially decreased the biofilm biomass,with nearly 4 logs of reduction in colony-forming units(CFUs).Furthermore,there was no change in the extent of the CFU reduction after passaging the survived bacteria with repeated exposures to the DMAHDM resin.Therefore,the biofilm remained highly and similarly susceptible to the DMAHDM resin from passages 1 to 20,showing no sign of drug resistance.152
DMADDM caused a mild drug resistance in S.gordonii,while DMAHDM did notinducedrug resistance.Regarding the mechanism,DMADDMandDMAHDMaremembrane-active antibacterial agents that interact with bacteria membranes.The quaternary ammonium antibacterial mode of action is related to the alkyl chain length(CL).Longer chains can more readily penetrate bacterial cells,similar to a needle bursting a balloon.DMAHDM with a longer CL of 16 exhibited a stronger antibacterial potency than DMADDM with a CL of 12.153The results that S.gordonii had drug resistance to DMADDM,but not to DMAHDM,indicate that the drug-resistant ability in bacteria is related to CL.
![pagenumber_ebook=28,pagenumber_book=327](https://qkk.lw71.com/uploads/image/2018/4/53d5476e192b80aa1680b76d79bd2397.png)
Fig.8 Smart inhibition of bacteria without inducing drug resistance.a Minimal inhibitory concentration(MIC).Twenty passages were tested,and each passage used the surviving bacteria from the previous passage as inoculum.A twofold increase in MIC occurred for DMADDM and CHX,indicating drug resistance.However,DMAHDM had no drug resistance.b From 1 to 20 passages,S.gordonii biofilm CFU on DMAHDM resin maintained a 4 log reduction over that without DMAHDM,showing the same sensitivity with no drug resistance.In b,bars with dissimilar letters are significantly different from each other(P<0.05).(Adapted from ref.146,with permission.)
The way that bacteria develops resistance may be to congeal or thicken the bacterial membrane and thereby resist the destruction of biocide alkyl action and prevent membrane leakage.It is likely that DMAHDM with longer alkyl chains could penetrate the hydrophobic bacterial membrane to cause bacteria lysis.Therefore,it appears to be more difficult for bacteria to acquire resistance against longer chains.These results indicate that longer alkyl chains(1)have stronger antimicrobial potency and(2)can make it more difficult for bacteria to develop drug resistance.152In addition to the CL,other parameters,such as the quaternary amine charge density on resins143,153and multiple modes of action by combining multiple agents,154may also provide ways to suppress the ability of bacteria to acquire drug resistance and warrant further investigation.Therefore,intelligently tailoring material parameters may enable the design of smart dental resins to exert antibacterial functions without inducing drug resistance.Furthermore,the smart design of antibacterial dental materials may have applicability for bone engineering constructs to possess antibacterial activity,without inducing drug resistance,to combat infections in wounds while regenerating bone tissues.
SUMMARY
This article reviewed recent developmentsin novel smart biomaterials for hard tissue engineering and regeneration.The cutting-edge research included smart scaffolds and stem cell constructs for bone tissue engineering,smart DDSs,smart constructs for periodontal regeneration,smart dental resins that respond to pH to protect tooth structures,smart pH-sensitive materials to selectively inhibit acid-producing bacteria,smart resins to modulate biofilm species towards a healthy composition and smart tailoring of materials to avoid drug resistance.Smart biomaterials/drug delivery and stem cell methods for bone tissue engineering are also applicable to dentistry,including maxillofacial,periodontal and pulp regenerations.Moreover,some of the smart approaches being developed in the dental field are also applicable to bone tissue engineering.For example,smart materials for tooth remineralization may benefit treatments for osteoporosis.In addition,smart dental materials,which can suppress bacteria and modulate biofilm species without inducing drug resistance in oral bacteria,may have applicability to bone engineering with infection control in wound sites.One disadvantage is that there has been only a relatively small number of systems of smart biomaterials reported to date,thus limiting the choice of available compositions.Therefore,future efforts are required to develop more novel compositions with improved and better-controlled smartness and to translate the in vitro smartness properties to effective in vivo tissue repair and regeneration in animal models.Overall,the new generation of smart biomaterials provides exciting potential and is promising to substantially enhance hard tissue engineering and regenerative medicine efficacy.
采用实验室静态试验(无辐照)的方法进行测试,将经过严格筛选的NPN型晶体管BCX41和PNP型晶体管3CK3B各5只作为测试对象,分别用Q1,Q2,Q3,Q4,Q5表示,分别通过长线连接在系统上,系统通电5 min后,启动测量,每间隔10 s测量一次晶体管的直流增益hFEi。稳定性,即系统的测试精度w可依据式(3)计算,当w≤1%时,系统的测试精度就满足实验的应用要求。
ACKNOWLEDGEMENTS
We thank Drs.Mary Anne S.Melo,Lin Wang,Satoshi Imazato,Joseph M.Antonucci,Nancy J.Lin,Sheng Lin-Gibson and Laurence C.Chow for discussions.This work was supported by NIH R01DE17974(H.H.K.X.),NIH U01DE023752(J.S.),International Science and Technology Programme 2017HH0008(L.C.),National Natural Science Foundation of China NSFC 81400540(K.Z.),Beijing Municipal Administration of Hospitals'Youth Programme QML20151401(K.Z.),NSFC 81500879(N.Z.),Nova Programme xx2014B060(X.X.)and University of Maryland Dental School Bridging Fund(H.H.K.X.).
单因素分析结果显示治疗前低ADCtot值组患者的生存期长于高ADCtot值组患者(P=0.067,图2)。射波刀治疗后联合口服S-1患者生存期长于未口服S-1患者(P=0.018),差异有统计学意义。后期转移后接受其他治疗(譬如介入及静脉化疗等)的患者生存期长于未接受其他治疗手段的患者(P=0.23),胰腺体尾癌患者的生存期长于胰头癌患者(P=0.261),但差异均无统计学意义。装有胆管支架与未装胆管支架两组患者的生存期差异无统计学意义(P=0.779)[7]。
《宋词互见考》:“案此黄庭坚词,见《彊村丛书》本《山谷琴趣外编》。《能改斋漫录》云……即此词也。并有陈后山同韵和词。据此则为黄词明甚,《淮海词》收之,毛本《山谷词》删之,并误。”[7]271
ADDITIONAL INFORMATION
Competing interests:The authors declare no competing interests.
1.Holzapfel,B.M.et al.How smart do biomaterials need to be?A translational science and clinical point of view.Adv.Drug Deliv.Rev.65,581-603(2013).
2.Sohail,M.et al.Natural and synthetic polymer-based smart biomaterials for management of ulcerative colitis:a review of recent developments and future prospects.Drug Deliv.Transl.Res.https://doi.org/10.1007/s13346-018-0512-x(2018).
3.Khan,F.&Tanaka,M.Designing smart biomaterials for tissue engineering.Int.J.Mol.Sci.19,17(2018).
4.Lendlein,A.,Feng,Y.,Griipma,D.W.&Zhao,Y.Smart materials.Chemphyschem.https://doi.org/10.1002/cphc.201800578(2018).
5.Mikos,A.G.et al.Engineering complex tissues.Tissue Eng.12,3307-3339(2006).
6.Mao,J.J.,Vunjak-Novakovic,G.,Mikos,A.G.&Atala,A.Regenerative Medicine:Translational Approaches and Tissue Engineering(Artech House,Boston and London,2007).
7.Cutter,C.S.&Mehrara,B.J.Bone grafts and substitutes.J.Long.Term.Eff.Med.Implants 16,249-260(2006).
8.United States Bone and Joint Decade.The Burden of Musculoskeletal Diseases in the United States(American Academy of Orthopaedic Surgeons,Rosemont,IL,2008).
9.Shi,J.,Qi,W.&Cao,S.Biomimetic self-assembly of calcium phosphate templated by PNIPAAm nanogels for sustained smart drug delivery.Mater.Sci.Eng.C 32,1299-1306(2012).
10.Perez,R.A.,Won,J.E.,Knowles,J.C.&Kim,H.W.Naturally and synthetic smart composite biomaterials for tissue regeneration.Adv.Drug Deliv.Rev.65,471-496(2013).
11.United Nations,World Population Prospects:http://esa.un.org/unpd/wpp/exceldata/population.htm(2012).
12.Beazoglou,T.et al.Economic impact of regulating the use of amalgam restorations.Public Health Rep.122,657-663(2007).
13.Saunders,R.H.&Meyerowitz,C.Dental caries in older adults.Dent.Clin.North Am.49,293-308(2005).
14.Zaura,E.&ten Cate,J.M.Towards understanding oral health.Caries Res.49,55-61(2015).
15.Sakaguchi,R.L.Review of the current status and challenges for dental posterior restorative composites:clinical,chemistry,and physical behavior considerations.Summary of discussion from the portland composites symposium(pocos)June 17-19,2004,oregon health and science university,portland,oregon.Dent.Mater.21,3-6(2005).
16.Jokstad,A.,Bayne,S.,Blunck,U.,Tyas,M.&Wilson,N.Quality of dental restorations.FDI Commission Project 2-95.Int.Dent.J.51,117-158(2001).
17.O'Brien,F.J.Biomaterials&scaffolds for tissue engineering.Mater.Today 14,88-95(2005).
18.Oest,M.E.,Dupont,K.M.,Kong,H.J.,Mooney,D.J.&Guldberg,R.E.Quantitative assessment of scaffold and growth factor-mediated repair of critically sized bone defects.J.Orthop.Res.25,941-950(2007).
19.Tatara,A.M.&Mikos,A.G.Tissue engineering in orthopaedics.J.Bone Joint Surg.Am.98,1132-1139(2016).
20.Motamedian,S.R.,Hosseinpour,S.,Ahsaie,M.G.&Khojasteh,A.Smart scaffolds in bone tissue engineering:a systematic review of literature.World J.Stem Cells 7,657-668(2015).
21.Kaigler,D.,Wang,Z.,Horger,K.,Mooney,D.J.&Krebsbach,P.H.VEGF scaffolds enhance angiogenesis and bone regeneration in irradiated osseous defects.J.Bone Miner.Res.21,735-744(2006).
22.Kim,H.D.et al.Biomimetic materials and fabrication approaches for bone tissue engineering.Adv.Healthc.Mater.6 https://doi.org/10.1002/adhm.201700612(2017).
23.Murphy,W.L.,McDevitt,T.C.&Engler,A.J.Materials as stem cell regulators.Nat.Mater.13,547-557(2014).
24.Franz,S.,Rammelt,S.,Scharnweber,D.&Simon,J.C.Immune responses to implants-a review of the implications for the design of immunomodulatory biomaterials.Biomaterials 32,6692-6709(2011).
25.Wu,T.,Yu,S.,Chen,D.&Wang,Y.Bionic design,materials and performance of bone tissue scaffolds.Materials 10,1187(2017).
26.Mittal,A.,Negi,P.,Garkhal,K.,Verma,S.&Kumar,N.Integration of porosity and bio-functionalization to form a 3D scaffold:cell culture studies and in vitro degradation.Biomed.Mater.5,045001(2010).
27.Shi,J.P.et al.A porous scaffold design method for bone tissue engineering using triply periodic minimal surfaces.IEEE Access 6,1015-1022(2018).
28.Chung,L.,Maestas,D.R.Jr,Housseau,F.&Elisseeff,J.H.Key players in the immune response to biomaterial scaffolds for regenerative medicine.Adv.Drug Deliv.Rev.114,184-192(2017).
29.Chen,Z.et al.Tuning chemistry and topography of nanoengineered surfaces to manipulate immune response for bone regeneration applications.ACS Nano 11,4494-4506(2017).
30.Li,W.A.et al.The effect of surface modification of mesoporous silica micro-rod scaffold on immune cell activation and infiltration.Biomaterials 83,249-256(2016).
31.Liu,X.&Ma,P.X.Phase separation,pore structure,and properties of nano fibrous gelatin scaffolds.Biomaterials 30,4094-4103(2009).
32.Liu,X.et al.Biomimetic nanofibrous gelatin/apatite composite scaffolds for bone tissue engineering.Biomaterials 30,2252-2258(2009).
33.Sachar,A.et al.Osteoblasts responses to three-dimensional nanofibrous gelatin scaffolds.J.Biomed.Mater.Res.A 100,3029-3041(2012).
34.Hu,Z.,Ma,C.,Rong,X.,Zou,S.&Liu,X.Immunomodulatory ECM-like microspheres for accelerated bone regeneration in diabetes mellitus.ACS Appl.Mater.Interfaces 10,2377-2390(2018).
35.Zeng,D.et al.Theosteoimmunomodulatory properties of MBG scaffold coated with amino functional groups.Artif.Cells Nanomed.Biotechnol.30,1-11(2017).
36.Chen,Z.T.et al.Osteoimmunomodulatory properties of magnesium scaffolds coated with b-tricalcium phosphate.Biomaterials 35,8553e8565(2014).
37.Huang,W.M.,Yang,B.,Zhao,Y.&Ding,Z.Thermo-moisture responsive polyurethane shape-memory polymer and composites:a review.J.Mater.Chem.20,3367-3381(2010).
38.Buckley,P.R.et al.Inductively heated shape memory polymer for the magnetic actuation of medical devices.IEEE Trans.Biomed.Eng.53,2075-2083(2006).
39.Mohr,R.et al.Initiation of shape-memory effect by inductive heating of magnetic nanoparticles in thermoplastic polymers.Proc.Natl Acad.Sci.USA 103,3540-3545(2006).
40.Lendlein,A.,Jiang,H.,Junger,O.&Langer,R.Light-induced shape-memory polymers.Nature 434,879-882(2005).
41.Yakacki,C.M.&Gall,K.in Shape-Memory Polymers(Springer,Berlin,Heidelberg,2010).
42.Langer,R.&Tirrell,D.A.Designing materials for biology and medicine.Nature 428,487-492(2004).
43.Montgomery,M.et al.Flexible shape-memory scaffold for minimally invasive delivery of functional tissues.Nat.Mater.16,1038-1046(2017).
44.An,J.,Teoh,J.E.M.,Suntornnond,R.&Chee,K.C.Design and 3D printing of scaffolds and tissues.Engineering 1,261-268(2015).
45.Liu,X.et al.Delivery of growth factors using a smart porous nanocomposite scaffold to repair a mandibular bone defect.Biomacromolecules 15,1019-1030(2014).
46.Miao,S.,Zhu,W.,Castro,N.J.,Leng,J.&Zhang,L.G.Four-dimensional printing hierarchy scaffolds with highly biocompatible smart polymers for tissue engineering applications.Tissue Eng.Part C Methods 22,952-963(2016).
47.Hendrikson,W.J.et al.Towards 4D printed scaffolds for tissue engineering:exploiting 3D shape memory polymers to deliver time-controlled stimulus on cultured cells.Biofabrication 9,031001(2017).
48.Markx,G.H.The use of electric fields in tissue engineering.Organogenesis 4,11-17(2008).
49.Singh,J.,Rani,S.,Rohini&Parida,A.Generation of piezoElectricity from the human body.2014 Annual International Conference on Emerging Research Areas:Magnetics,Machines and Drives(AICERA/iCMMD)(2014).
50.Ribeiro,C.et al.Enhanced proliferation of pre-osteoblastic cells by dynamic piezoelectric stimulation.RSC Adv.2,11504-11509(2012).
51.Dubey,A.K.,Balani,K.&Basu,B.in Nanomedicine:Technologies and Applications 537-570(Woodhead Publishing Ltd,2012).
52.Rajabi,A.H.,Jaffe,M.&Arinzeh,T.L.Piezoelectric materials for tissue regeneration:A review.Acta Biomater.24,12-23(2015).
53.More,N.&Kapusetti,G.Piezoelectric material-a promising approach for bone and cartilage regeneration.Med.Hypotheses 108,10-16(2017).
54.Damaraju,S.M.et al.Three-dimensional piezoelectric fibrous scaffolds selectively promote mesenchymal stem cell differentiation.Biomaterials 149,51-62(2017).
55.Augustine,R.et al.Electrospun poly(vinylidene fluoride-tri fluoroethylene)/zinc oxide nanocomposite tissue engineering scaffolds with enhanced cell adhesion and blood vessel formation.Nano Res.10,3358-3376(2017).
56.Tang,Y.et al.Fabrication and in vitro biological properties of piezoelectric bioceramics for bone regeneration.Sci.Rep.7,43360(2017).
57.Sun,G.&Mao,J.J.Engineering dextran-based scaffolds for drug delivery and tissue repair.Nanomedicine(Lond.)7,1771-1184(2012).
58.Samorezov,J.E.&Alsberg,E.Spatial regulation of controlled bioactive factor delivery for bone tissue engineering.Adv.Drug Deliv.Rev.84,45-67(2015).
59.Lee,E.J.et al.Application of materials as medical devices with localized drug delivery capabilities for enhanced wound repair.Prog.Mater.Sci.89,392-410(2017).
60.Kretlow,J.D.,Hacker,M.C.,Klouda,L.,Ma,B.B.&Mikos,A.G.Synthesis and characterization of dual stimuli responsive macromers based on poly(N-isopropylacrylamide)and poly(vinylphosphonic acid).Biomacromolecules 11,797-805(2010).
61.Safari,J.&Zarnegar,Z.Advanced drug delivery systems:nanotechnology of health design.A review.J.Saudi Chem.Soc.18,85-99(2014).
62.Liu,D.,Yang,F.,Xiong,F.&Gu,N.The smart drug delivery system and its clinical potential.Theranostics 6,1306-1323(2016).
63.Kelley,E.G.,Albert,J.N.,Sullivan,M.O.&Epps,T.H.3rd Stimuli-responsive copolymer solution and surface assemblies for biomedical applications.Chem.Soc.Rev.42,7057-7071(2013).
64.Mura,S.,Nicolas,J.&Couvreur,P.Stimuli-responsive nanocarriers for drug delivery.Nat.Mater.12,991-1003(2013).
65.Gu,Z.Introduction to special issue on“Responsive Materials and Systems:Toward Smart and Precision Medications”.Bioeng.Transl.Med.1,235-236(2016).
66.Kondiah,P.J.et al.A review of injectable polymeric hydrogel systems for application in bone tissue engineering.Molecules 21,E1580(2016).
67.Mohd Amin,M.C.,Ahmad,N.,Pandey,M.&Jue Xin,C.Stimuli-responsive bacterial cellulose-g-poly(acrylic acid-co-acrylamide)hydrogels for oral controlled release drug delivery.Drug Dev.Ind.Pharm.40,1340-1349(2014).
68.Ashley,G.W.,Henise,J.,Reid,R.&Santi,D.V.Hydrogel drug delivery system with predictable and tunable drug release and degradation rates.Proc.Natl Acad.Sci.USA 110,2318-2323(2013).
69.Horev,B.et al.pH-activated nanoparticles for controlled topical delivery of farnesol to disrupt oral biofilm virulence.ACS Nano 9,2390-2404(2015).
70.Li,F.,Zhu,Y.&Wang,Y.Dual-responsive drug delivery system with real time tunable release behavior.Micro.Mesopor.Mater.200,46-51(2014).
71.Suri,S.S.,Fenniri,H.&Singh,B.Nanotechnology-based drug delivery systems.J.Occup.Med.Toxicol.2,16(2007).
72.Singh,R.&Lillard,J.W.Nanoparticle-based targeted drug delivery.Exp.Mol.Pathol.86,215-223(2009).
73.van Rijt,S.&Habibovic,P.Enhancing regenerative approaches with nanoparticles.J.R.Soc.Interface 14,20170093(2017).
74.Bharti,C.,Nagaich,U.,Pal,A.K.&Gulati,N.Mesoporous silica nanoparticles in target drug delivery system:a review.Int.J.Pharm.Investig.5,124-133(2015).
75.Karimi,M.et al.Smart micro/nanoparticles in stimulus-responsive drug/gene delivery systems.Chem.Soc.Rev.45,1457-1501(2016).
76.Karimi,M.,Mirshekari,H.,Aliakbari,M.,Sahandi-Zangabad,P.&Michael,R.H.Smart mesoporous silica nanoparticles for controlled-release drug delivery.Nanotechnol.Rev.195,(2015).https://doi.org/10.1515/ntrev-2015-0057.
77.Luo,Z.et al.Time-responsive osteogenic niche of stem cells:a sequentially triggered,dual-peptide loaded,alginate hybrid system for promoting cell activity and osteo-differentiation.Biomaterials 163,25-42(2018).
78.Pellowe,A.&Gonzalez,A.Extracellular matrix biomimicry for the creation of investigational and therapeutic devices.Wiley Interdiscip.Rev.Nanomed.Nanobiotechnol.8,5-22(2016).
79.Ma,P.X.Biomimetic materials for tissue engineering.Adv.Drug Deliv.Rev.60,184-198(2008).
80.Tsiapalis,D.,De Pieri,A.,Biggs,M.,Pandit,A.&Zeugolis,D.I.Biomimetic bioactive biomaterials:the next generation of implantable devices.ACS Biomater.Sci.Eng.3,1172-1174(2017).
81.Fernandez-Yague,M.A.et al.Biomimetic approaches in bone tissue engineering:Integrating biological and physicomechanical strategies.Adv.Drug Deliv.Rev.84,1-29(2015).
82.Sant,S.,Hancock,M.J.,Donnelly,J.P.,Iyer,D.&Khademhosseini,A.Biomimetic gradient hydrogels for tissue engineering.Can.J.Chem.Eng.88,899-911(2010).
83.Sheikhpour,M.,Barani,L.&Kasaeian,A.Biomimetics in drug delivery systems:a critical review.J.Control Release 253,97-109(2017).
84.Lee,N.,Robinson,J.&Lu,H.Biomimetic strategies for engineering composite tissues.Curr.Opin.Biotechnol.40,64-74(2016).
85.Phipps,M.C.,Monte,F.,Mehta,M.&Kim,H.K.W.Intraosseous delivery of bone morphogenic protein-2 using a self-assembling peptide hydrogel.Biomacromolecules 17,2329-2336(2016).
86.Feng,C.et al.Lotus root-like biomimetic materials for cell delivery and tissue regeneration.Adv.Sci.4,1700401(2017).
87.Pihlstrom,B.L.,Michalowicz,B.S.&Johnson,N.W.Periodontal diseases.Lancet 366,1809(2005).
88.Monsarrat,P.et al.Concise review:mesenchymal stromal cells used for periodontal regeneration:a systematic review.Stem Cells Transl.Med.3,768-774(2014).
89.Khosla,S.,Westendorf,J.J.&Mödder,U.I.Concise review:insights from normal bone remodeling and stem cell-based therapies for bone repair.Stem Cells 28,2124(2010).
90.Chen,F.M.et al.A review on endogenous regenerative technology in periodontal regenerative medicine.Biomaterials 31,7892(2010).
91.Zhu,B.et al.Jawbone microenvironment promotes periodontium regeneration by regulating the function of periodontal ligament stem cells.Sci.Rep.7,40088(2017).
92.Subramaniam,S.,Fang,Y.H.,Sivasubramanian,S.,Lin,F.H.&Lin,C.P.Hydroxyapatite-calcium sulfate-hyaluronic acid composite encapsulated with collagenase as bone substitute for alveolar bone regeneration.Biomaterials 74,99-108(2016).
93.Dan,H.et al.The influence of cellular source on periodontal regeneration using calcium phosphate coated polycaprolactone scaffold supported cell sheets.Biomaterials 35,113-122(2014).
94.Bhattarai,G.,Poudel,S.B.,Kook,S.H.&Lee,J.C.Anti-inflammatory,antiosteoclastic,and antioxidant activities of genistein protect against alveolar bone loss and periodontal tissue degradation in a mouse model of periodontitis.J.Biomed.Mater.Res.A 105,2510-2521(2017).
95.Bhattarai,G.,Poudel,S.B.,Kook,S.H.&Lee,J.C.Resveratrol prevents alveolar bone loss in an experimental rat model of periodontitis.Acta Biomater.29,398-408(2016).
96.Chang,P.C.,Chien,L.Y.,Ye,Y.&Kao,M.J.Irradiation by light-emitting diode light as an adjunct to facilitate healing of experimental periodontitis in vivo.J.Periodontal Res.48,135-143(2013).
97.Xue,J.et al.Fabrication of drug-loaded anti-infective guided tissue regeneration membrane with adjustable biodegradation property.Colloids Surf.B Biointerfaces 135,846-854(2015).
98.Chu,C.,Deng,J.,Sun,X.,Qu,Y.&Man,Y.Collagen membrane and immune response in guided bone regeneration:recent progress and perspectives.Tissue Eng.Part B Rev.23,421-435(2017).
99.Hu,Z.,Ma,C.,Rong,X.,Zou,S.&Liu,X.Immunomodulatory ECM-like microspheres for accelerated bone regeneration in diabetes mellitus.ACS Appl.Mater.Interfaces 10,2377-2390(2018).2018.
100.Zhu,Y.et al.Bone regeneration with micro/nano hybrid-structured biphasic calcium phosphate bioceramics at segmental bone defect and the induced immunoregulation of MSCs.Biomaterials 147,133-144(2017).
101.Nivedhitha Sundaram,M.,Sowmya,S.,Deepthi,S.,Bumgardener,J.D.&Jayakumar,R.Bilayered construct for simultaneous regeneration of alveolar bone and periodontal ligament.J.Biomed.Mater.Res.B Appl.Biomater.104,761-770(2016).
102.Youse fi,A.M.,Hoque,M.E.,Prasad,R.G.&Uth,N.Current strategies in multiphasic scaffold design for osteochondral tissue engineering:A review.J.Biomed.Mater.Res.A 103,2460-2481(2015).
103.Wu,X.et al.Electrospun fibrous scaffolds combined with nanoscale hydroxyapatite induce osteogenic differentiation of human periodontal ligament cells.Int.J.Nanomed.9,4135-4143(2014).
104.Lee,C.H.et al.Three-dimensional printed multiphase scaffolds for regeneration of periodontium complex.Tissue Eng.A 20,1342-1351(2014).
105.Costa,P.F.et al.Advanced tissue engineering scaffold design for regeneration of the complex hierarchical periodontal structure.J.Clin.Periodontol.41,283-294(2014).
106.Vaquette,C.et al.A biphasic scaffold design combined with cell sheet technology for simultaneous regeneration of alveolar bone/periodontal ligament complex.Biomaterials 33,5560-5573(2012).
107.Carlo Reis,E.C.et al.Periodontal regeneration using a bilayered PLGA/calcium phosphate construct.Biomaterials 32,9244-9253(2011).
108.Han,P.,Ivanovski,S.,Crawford,R.&Xiao,Y.Activation of the canonical Wnt signaling pathway induces cementum regeneration.J.Bone Miner.Res.30,1160-1174(2015).
109.Needleman,I.G.,Worthington,H.V.,Giedrys-Leeper,E.&Tucker,R.J.Guided tissue regeneration for periodontal infra-bony defects.Cochrane Database Syst.Rev.2006,Cd001724(2006).
110.Xue,J.et al.Drug loaded homogeneous electrospun PCL/gelatin hybrid nanofi ber structures for anti-infective tissue regeneration membranes.Biomaterials 35,9395-9405(2014).
111.Cheng,C.F.,Wu,K.M.,Chen,Y.T.&Hung,S.L.Bacterial adhesion to antibioticloaded guided tissue regeneration membranes-a scanning electron microscopy study.J.Formos.Med.Assoc.114,35-45(2015).
112.Cheng,C.F.et al.Bacterial penetration through antibiotic-loaded guided tissue regeneration membranes.J.Periodontol.80,1471-1478(2009).
113.Basile,M.A.et al.Functionalized PCL/HA nanocomposites as microporous membranes for bone regeneration.Mater.Sci.Eng.C Mater.Biol.Appl.48,457-468(2015).
114.Xu,C.,Lei,C.,Meng,L.,Wang,C.&Song,Y.Chitosan as a barrier membrane material in periodontal tissue regeneration.J.Biomed.Mater.Res.B Appl.Biomater.100,1435-1443(2012).
115.Xu,S.et al.Preparation and in vitro biological evaluation of octacalcium phosphate/bioactive glass-chitosan/alginate composite membranes potential for bone guided regeneration.J.Nanosci.Nanotechnol.16,5577-5585(2016).
116.Li,W.,Ding,Y.,Yu,S.,Yao,Q.&Boccaccini,A.R.Multifunctional chitosan-45S5 bioactive glass-poly(3-hydroxybutyrate-co-3-hydroxyvalerate) microsphere composite membranes for guided tissue/bone regeneration.ACS Appl.Mater.Interfaces 7,20845-20854(2015).
117.Di Benedetto,A.,Gigante,I.,Colucci,S.&Grano,M.Periodontal disease:linking the primary inflammation to bone loss.Clin.Dev.Immunol.2013,503754(2013).
118.Sima,C.&Glogauer,M.Macrophage subsets and osteoimmunology:tuning of the immunological recognition and effector systems that maintain alveolar bone.Periodontol.2000 63,80-101(2013).
119.Gao,X.et al.Immunomodulatory role of stem cells from human exfoliated deciduous teeth on periodontal regeneration.Tissue Eng.Part A https://doi.org/10.1089/ten(2018).
120.Requicha,J.F.et al.A tissue engineering approach for periodontal regeneration based on a biodegradable double-layer scaffold and adipose-derived stem cells.Tissue Eng.Part A 20,2483-2492(2014).
121.Sowmya,S.et al.Tri-layered nanocomposite hydrogel scaffold for the concurrent regeneration of cementum,periodontal ligament,and alveolar bone.Adv.Healthc.Mater.6,(2017).
122.Van Houte,J.Role of micro-organisms in caries etiology.J.Dent.Res.73,v672-v681(1994).
123.Featherstone,J.D.B.The continuum of dental caries-evidence for a dynamic disease process.J.Dent.Res.83,C39-C42(2004).
124.Deng,D.M.&ten Cate,J.M.Demineralization of dentin by Streptococcus mutans biofilms grown in the constant depth film fermentor.Caries Res.38,54-61(2004).
125.Totiam,P.,Gonzalez-Cabezas,C.,Fontana,M.R.&Zero,D.T.A new in vitro model to study the relationship of gap size and secondary caries.Caries Res.41,467-473(2007).
126.Thylstrup,A.&Fejerskov,O.Textbook of Cariology(Munksgaard,Copenhagen,Denmark,1986).
127.Dawes,C.What is the critical pH and why does a tooth dissolve in acid?J.Can.Dent.Assoc.69,722-724(2003).
128.Weir,M.D.et al.Effect of calcium phosphate nanocomposite on in vitro remineralization of human dentin lesions.Dent.Mater.33,1033-1044(2017).
129.Xu,H.H.,Moreau,J.L.,Sun,L.&Chow,L.C.Nanocomposite containing amorphous calcium phosphate nanoparticles for caries inhibition.Dent.Mater.27,762-769(2011).
130.Weir,M.D.,Chow,L.C.&Xu,H.H.Remineralization of demineralized enamel via calcium phosphate nanocomposite.J.Dent.Res.91,979-984(2012).
131.Melo,M.A.S.,Weir,M.D.,Rodrigues,L.K.&Xu,H.H.Novel calcium phosphate nanocomposite with caries-inhibition in a human in situ model.Dent.Mater.29,231-240(2013).
132.Xie,X.J.et al.Novel dental adhesive with triple benefits of calcium phosphate recharge,protein-repellent and antibacterial functions.Dent.Mater.33,553-563(2017).
133.Nizet,V.et al.Innate antimicrobial peptide protects the skin from invasive bacterial infection.Nature 414,454-457(2001).
134.Li,L.et al.Design and characterization of an acid-activated antimicrobial peptide.Chem.Biol.Drug Des.75,127-132(2010).
135.Yang,Y.et al.pH-sensitive compounds for selective inhibition of acid-producing bacteria.ACS Appl.Mater.Interfaces 10.1021/acsami.8b01089(2018).
136.Imazato,S.et al.An in vivo evaluation of bonding ability of comprehensive antibacterial adhesive system incorporating MDPB.Dent.Mater.23,170-176(2007).
137.Imazato,S.Bioactive restorative materials with antibacterial effects:new dimension of innovation in restorative dentistry.Dent.Mater.J.28,11-19(2009).
138.Imazato,S.et al.Therapeutic polymers for dental adhesives:loading resins with bio-active components.Dent.Mater.30,97-104(2014).
139.Beyth,N.et al.Polyethyleneimine nanoparticles incorporated into resin composite cause cell death and trigger biofilm stress in vivo.Proc.Natl Acad.Sci.USA 107,22038-22043(2014).
140.Li,F.et al.Effects of a dental adhesive incorporating antibacterial monomer on the growth,adherence and membrane integrity of Streptococcus mutans.J.Dent.37,289-296(2009).
141.Cheng,L.et al.Dental plaque microcosm biofilm behavior on calcium phosphate nanocomposite with quaternary ammonium.Dent.Mater.28,853-862(2012).
142.Li,F.,Weir,M.D.&Xu,H.H.Effects of quaternary ammonium chain length on antibacterial bonding agents.J.Dent.Res.92,932-938(2013).
143.Zhou,H.et al.Dental plaque microcosm response to bonding agents containing quaternary ammonium methacrylates with different chain lengths and charge densities.J.Dent.41,1122-1131(2013).
144.Marsh,P.D.,Head,D.A.&Devine,D.A.Dental plaque as a biofilm and a microbial community-Implications for treatment.J.Oral Biosci.57,185-191(2015).
145.Zhang,K.et al.Effect of antibacterial dental adhesive on multispecies biofilms formation.J.Dent.Res.94,622-629(2015).
146.Wang,H.H.et al.Novel dental composite with capability to suppress cariogenic species and promote non-cariogenic species in oral biofilms.Mater.Sci.Eng.C Mater.Biol.Appl.(2018,accepted for publication).
147.Hegstad,K.et al.Does the wide use of quaternary ammonium compounds enhance the selection and spread of antimicrobial resistance and thus threaten our health?Microb.Drug Resist.16,91-104(2010).
148.Ioannou,C.J.,Hanlon,G.W.&Denyer,S.P.Action of disinfectant quaternary ammonium compounds against Staphylococcus aureus.Antimicrob.Agents Chemother.51,296-306(2007).
149.Bragg,R.et al.Bacterial resistance to quaternary ammonium compounds(QAC)disinfectants.Adv.Exp.Med.Biol.808,1-13(2014).
150.Kitagawa,H.et al.Evolution of resistance to cationic biocides in Streptococcus mutans and Enterococcus faecalis.J.Dent.47,18-22(2016).
151.Wang,S.P.et al.Do quaternary ammonium monomers induce drug resistance in cariogenic,endodontic and periodontal bacterial species?Dent.Mater.33,1127-1138(2017).
152.Wang,S.P.et al.Drug resistance of oral bacteria to new antibacterial dental monomer dimethylaminohexadecyl methacrylate.Sci.Rep.8,5509(2018).
153.Zhou,H.et al.Three-dimensional biofilm evaluation on bonding agents containing quaternary ammonium methacrylates with different chain lengths.Int.J.Oral Sci.6,77-86(2014).
154.Zhang,N.et al.Orthodontic cement with protein-repellent and antibacterial properties and the release of calcium and phosphate ions.J.Dent.50,51-59(2016).